PENTAMID AHT GV30 H MOS non-colored
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID AHT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CuBOVO_PENTAMIDAHTGV30HMOSnoncolored.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyamide 4.6,easy flow, 30% glass fiber reinforced, modified with MoS2 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.42 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.90 | -- | % | ISO 294-4 |
| Flow | 0.65 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.3 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | ISO 62 |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10300 | 6150 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 195 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.8 | 7.0 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | 19 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 75 | 85 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 280 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 275 | -- | °C | ISO 75-2/A |
| Melting Temperature | 285 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength | 26 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.40 | -- | IEC 60250 | |
| Comparative Tracking Index | 250 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA46, MHRS, 18-100 N, GF30+X1 | -- | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.060 - 0.14 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 295 - 320 | °C | |
| Middle Temperature | 305 - 330 | °C | |
| Front Temperature | 310 - 320 | °C | |
| Processing (Melt) Temp | 305 - 325 | °C | |
| Mold Temperature | 80 - 120 | °C | |
| Injection Pressure | 85.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melthene® -M M5321 | TOSOH Corporation | Polyolefin, Unspecified | Melthene® -M |
| Sympoxy™ 1873 | Hapco Inc. | Epoxy | Sympoxy™ |
| WELLAMID Nylon 6000 GS 20 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| ASTALAC™ ABS X13 | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| Halene L LLT12 | Haldia Petrochemicals Ltd. | LLDPE | Halene L |