Edgetek™ X AS/018 NC704
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CtworD_Edgetek-X-AS-018-NC704.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS Resin |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 55.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2500 | MPa | ASTM D790 |
| Flexural Strength 3 | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 250 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 200 - 240 | °C | |
| Middle Temperature | 200 - 240 | °C | |
| Front Temperature | 200 - 240 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 35.2.0 | Marco Polo International, Inc. | PP Copolymer | MARPOL® COPP |
| T-Blend® TPR-F78B | TSRC Corporation | SEBS | T-Blend® |
| FLEXCHEM™ 5553 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| Edgetek™ CY-1000 UV FR V0 | PolyOne Corporation | PC+ABS | Edgetek™ |
| NHU-PPS 21310C/F | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |