NEXUS ABS ABSLG3030
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Nexus Resin Group, LLC. |
| Trademark: | NEXUS ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CtVEUt_NEXUS-ABS-ABSLG3030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Molding Grade ABS, Low Gloss |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2280 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 41.4 | MPa | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 82.2 | °C | ASTM D648 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | < 60 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 188 to 218 | °C | |
| Middle Temperature | 204 to 232 | °C | |
| Front Temperature | 218 to 246 | °C | |
| Nozzle Temperature | 218 to 274 | °C | |
| Processing (Melt) Temp | 218 to 274 | °C | |
| Mold Temperature | 37.8 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.689 | MPa | |
| Screw Speed | 25 to 75 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nycal™ 1850R33T2H | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| Celstran® PA66-GF50-02 P7 | Celanese Corporation | Nylon 66 | Celstran® |
| GERMADUR N | Kunststoff-Kontor-Hamburg GmbH | PBT | GERMADUR |
| EPAMOULD 685A56 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| Pro-fax 6331NW | LyondellBasell Industries | PP Homopolymer | Pro-fax |