| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Eastalloy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CtSGtG_EastalloyDA510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Eastalloy™ Polymer DA510 is a clear copolyester/polycarbonate alloy. This product has good physical properties. These include good impact strength, chemical resistance, heat resistance, dimensional stability, and low mold shrinkage. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 50.0 | MPa | ASTM D638 |
| Fracture | 56.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.5 | % | ASTM D638 |
| Fracture | 200 | % | ASTM D638 |
| Flexural Modulus | 2100 | MPa | ASTM D790 |
| Flexural Strength | 76.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 91 | J/m | ASTM D256 |
| 23°C | No Break | ASTM D256 | |
| Unnotched Izod Impact | ASTM D4812 | ||
| -40°C | No Break | ASTM D4812 | |
| 23°C | No Break | ASTM D4812 | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Energy at Peak Load | 49.0 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 55.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 90.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 77.0 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total) | 86.0 | % | ASTM D1003 |
| Haze | 0.50 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 88 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 266 - 288 | °C | |
| Mold Temperature | 27 - 60 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| COSMOTHENE® F210-6 | TPC, The Polyolefin Company (Singapore) Pte Ltd | LDPE | COSMOTHENE® |
| IDI BMC 44-10 | IDI Composites International | TS, Unspecified | IDI BMC |
| LNP™ STAT-KON™ RFD03 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| LNP™ LUBRICOMP™ 9X06084 compound | SABIC Innovative Plastics Europe | Nylon 46 | LNP™ LUBRICOMP™ |
| StarGrip-X® 5055-1000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarGrip-X® |