3M™ Dyneon™ PTFE Compound TF 3105
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ PTFE Compound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ct78OU_3M-Dyneon-PTFE-Compound-TF-3105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.20 | g/cm³ | ASTM D4745-06 |
| Apparent Density | 0.50 | g/cm³ | ASTM D4894-07 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D4894-07 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness 1(Shore D) | 67 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break) | 19.0 | MPa | ASTM D4745-06 |
| Tensile Elongation 3(Break) | 280 | % | ASTM D4745-06 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | 50.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | < 365 |
| Note Message | |
|---|---|
| 1 . | Measured on sintered moldings |
| 2 . | Measured on sintered moldings |
| 3 . | Measured on sintered moldings |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOYOBO Urethane E2090A | TOYOBO America, Inc. | PUR-Capro | TOYOBO Urethane |
| Bayflex® 110-50 (24% Mineral) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| DENITER C | Vamp Tech | PC+PBT | DENITER |
| GAPEX® RPP30EB44BK | Ferro Corporation | PP Homopolymer | GAPEX® |
| LNP™ THERMOTUF™ VF008 compound | SABIC Innovative Plastics | Nylon, Unspecified | LNP™ THERMOTUF™ |