Ultramid 8333G HI HS BK-102 is a 33% glass reinforced, impact modified PA6 injection molding compound pigmented black developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics. Applications Ultramid 8333G HI HS BK-102 is generally recommended for application such as front wheel chair wheels, bicycle wheels, power tool housings, chain saw housings, clips and fasteners, hose clamps and window hardware. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.34 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | |
| Water Absorption | ||||
| 24 hr | 0.90 | -- | % | ASTM D570 |
| 23°C, 24 hr | 0.90 | -- | % | ISO 62 |
| Saturation | 5.5 | -- | % | ASTM D570 |
| Saturation, 23°C | 5.5 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.5 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9100 | 4610 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Break, 23°C | 150 | 90.0 | MPa | ASTM D638 |
| Break, 23°C | 140 | 90.0 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Break, 23°C | 3.0 | -- | % | ASTM D638 |
| Break, 23°C | 3.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 8140 | -- | MPa | ASTM D790 |
| 23°C | 7500 | 5030 | MPa | ISO 178 |
| Flexural Strength | ||||
| 23°C | 240 | -- | MPa | ASTM D790 |
| 23°C | 210 | 120 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 18 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 71 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact | ||||
| -40°C | 110 | -- | J/m | ASTM D256 |
| 23°C | 210 | -- | J/m | ASTM D256 |
| -40°C | 13 | -- | kJ/m² | ISO 180 |
| 23°C | 19 | -- | kJ/m² | ISO 180 |
| Drop Impact Resistance (23°C) | 5.29 | -- | J | Internal Method |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| RTI Elec | UL 746 | |||
| 0.800 mm | 140 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C | |
| RTI Imp | UL 746 | |||
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.800 mm | 130 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 245 to 275 | °C | |
| Middle Temperature | 260 to 285 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| METLBOND® 2550 | Cytec Industries Inc. | MAH-g | METLBOND® |
| Sylvin 8215-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Axiall PVC 1901 Clear 7002 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Chemlon® E-66 GF50 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Fiberfil® J-60/30/E3 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |