Nypol® PA A3 G10 NTLA010 NR452
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cs1PgZ_Nypol-PA-A3-G10-NTLA010-NR452.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural reinforced with 10% of fiberglass, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.21 | -- | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | |||
| Saturation | 7.1 | -- | % | |
| Equilibrium | 2.2 | -- | % | |
| Ash Content | 8.0 to 12 | -- | % | ASTM D2584 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deformation Under Load - 27.6 MPa (50°C) | 1.1 | -- | % | ASTM D621 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5500 | 3500 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | |||
| Break | 118 | 75.0 | MPa | |
| -- | 120 | 80.0 | MPa | |
| Tensile Elongation (Break) | 3.0 to 3.2 | 8.0 to 12 | % | ASTM D638 |
| Flexural Modulus | 5300 | 3000 | MPa | ASTM D790 |
| Flexural Strength | 190 | 140 | MPa | ASTM D790 |
| Shear Strength | 75.0 | -- | MPa | ASTM D732 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 4.0 | 4.0 | kJ/m² | |
| 23°C | 4.5 | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 30 | 30 | kJ/m² | |
| 23°C | 32 | 70 | kJ/m² | |
| Notched Izod Impact | 48 | 52 | J/m | ASTM D256 |
| Notched Izod Impact (Area) | ASTM D256 | |||
| -40°C | 4.00 | 3.00 | kJ/m² | |
| 23°C | 4.50 | 4.00 | kJ/m² | |
| Unnotched Izod Impact (Area) | ASTM D256 | |||
| -30°C | 35.0 | 28.0 | kJ/m² | |
| 23°C | 40.0 | 55.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 230 | -- | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 65.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ARE-72D | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| TECHNYL STAR™ AFX 218 V60 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL STAR™ |
| INELEC PA612CF30 | Infinity LTL Engineered Compounds | Nylon 6/12 | INELEC |
| OXPEKK® MG230C | Oxford Performance Materials, Inc. | PEKK | OXPEKK® |
| Sylvin 2971-92 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |