Rotec® ABS SE 3
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Rotec® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cre444_Rotec-ABS-SE-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Rotec®ABS SE 3 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in Europe and is processed by extrusion or injection molding. Rotec®The main characteristics of ABS SE 3 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.50 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 46.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 15 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2450 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 90 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 99.0 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.18 | W/m/K | DIN 52612 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 210 - 250 | °C | |
| Middle Temperature | 210 - 250 | °C | |
| Front Temperature | 210 - 250 | °C | |
| Processing (Melt) Temp | < 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Screw rotation speed: moderate to highBack pressure: low to moderateInjection pressure: tool depending |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 190 - 210 | °C | |
| Cylinder Zone 2 Temp. | 190 - 210 | °C | |
| Cylinder Zone 3 Temp. | 190 - 210 | °C | |
| Cylinder Zone 4 Temp. | 190 - 210 | °C | |
| Cylinder Zone 5 Temp. | 190 - 210 | °C | |
| Melt Temperature | < 245 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V836 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Nivionplast® B 273B NATURALE | SO.F.TER. SPA | Nylon 6 | Nivionplast® B |
| Bakelite® PF 6510 | Hexion Inc. | Phenolic | Bakelite® |
| LNP™ LUBRICOMP™ WFL33 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |
| Dryflex® SE 80A001N U | ELASTO | SEBS | Dryflex® |