Ultradur® S 4090 G4
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CrMAfq_Ultradur-S-4090-G4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultradur S 4090 G4 is a 20% glass reinforced PBT+ASA blend. It produces moldings with good surface finish,is resistant to chemicals and stress cracking, and has low shrinkage and warpage. Applications Applications include highly stressed equipment housings in the automotive, electrical and household sectors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.18 mm | 0.30 | % | |
| Across Flow | 0.74 | % | ISO 294-4 |
| Flow | 0.43 | % | ISO 294-4 |
| Water Absorption | |||
| Saturation | 0.40 | % | ASTM D570 |
| Saturation, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 105.0 | ml/g | ISO 1628 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6900 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Break, 23°C | 100 | MPa | ASTM D638, ISO 527-2 |
| Break, -40°C | 160 | MPa | ISO 527-2 |
| Break, 80°C | 68.0 | MPa | ISO 527-2 |
| Break, 121°C | 42.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 2.5 | % | ASTM D638, ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 5300 | MPa | |
| 1000 hr | 4700 | MPa | |
| Flexural Modulus | |||
| 23°C | 6100 | MPa | ASTM D790 |
| 23°C | 6400 | MPa | ISO 178 |
| Flexural Strength (23°C) | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 43 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact | |||
| -40°C | 68 | J/m | ASTM D256 |
| 23°C | 80 | J/m | ASTM D256 |
| 23°C | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 216 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 205 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 194 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 160 | °C | ISO 75-2/A |
| Peak Melting Temperature | 223 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | ||
| 0.710 mm | 130 | °C | |
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 0.710 mm | 90.0 | °C | |
| 1.50 mm | 90.0 | °C | |
| 3.00 mm | 90.0 | °C | |
| RTI Str | UL 746 | ||
| 0.710 mm | 130 | °C | |
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 1 | 1.0E+14 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | |||
| 1.50 mm | > 1.0E+13 | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.70 | ||
| 1 MHz | 3.60 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 0.019 | ||
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.710 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | < 1.00 | MPa |
| Note Message | |
|---|---|
| 1 . | 1.5 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONYL 4009EPG15 | POLYROCKS CHEMICAL CO., LTD | Nylon 6 | PONYL |
| SILVER® SA-2101 | Guangdong Silver Age Sci & Tech. Co., Ltd | SEBS | SILVER® |
| NORYL GTX™ GTX8120P resin | SABIC Innovative Plastics Europe | PPE+PS+Nylon | NORYL GTX™ |
| ALKAMIX™ MB-6007 | Marplex Australia Pty. Ltd. | Unspecified | ALKAMIX™ |
| RTP 399 X 141380 B | RTP Company | PC | RTP |