Badamid® LB70 GF40 TM-Z3
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CqZxpi_Badamid-LB70-GF40-TM-Z3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® LB70 GF40 TM-Z3 is a Polyamide 6 (Nylon 6) material filled with 40% glass fiber. It is available in Europe. Primary attribute of Badamid® LB70 GF40 TM-Z3: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.0 to 6.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.5 to 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11500 | 6500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 165 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.0 | 10 | % | ISO 527-2/5 |
| Flexural Stress (23°C) | 245 | 130 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | -- | kJ/m² | |
| 23°C | 20 | 35 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | -- | kJ/m² | |
| 23°C | 100 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 222 | -- | °C | ISO 3146 |
| CLTE | DIN 53752 | |||
| Flow | 2.0E-5 to 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 to 7.0E-5 | -- | cm/cm/°C | |
| Maximum Service Temperature | 180 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.80 | 6.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.15 | IEC 60250 | |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V914 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| AIE PET 40G6 | Asia International Enterprise (Hong Kong) Limited | PET | AIE PET |
| Carbotex K-50MRA | Kotec Corporation | PC | Carbotex |
| KOPA® KN173HI3RBL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| LNP™ LUBRICOMP™ QCL349 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |