TRIBOCOMP® PBT GF30 TS0
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CqAqBG_TRIBOCOMP-PBT-GF30-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP®PBT GF30 TS0 is a polybutene terephthalate (PBT) product. The filler is 15% ptfe fiber and 30% glass fiber reinforced material. It is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| 23°C | 10500 | MPa | ISO 527-2 |
| 90°C | 5600 | MPa | ISO 527-2 |
| 120°C | 4500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 130 | MPa | ISO 527-2 |
| Fracture, 90°C | 80.0 | MPa | ISO 527-2 |
| Fracture, 120°C | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 185 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | ||
| Dynamic | 0.23 | ASTM D3702 | |
| Static | 0.18 | ASTM D3702 | |
| Wear Factor | 22.0 | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.9E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.30 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric Strength (2.00 mm) | 29 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 325 | V | IEC 60112 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 2.0E-3 | % | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 220 - 260 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Nozzle Temperature | 240 - 270 | °C | |
| Processing (Melt) Temp | < 270 | °C | |
| Mold Temperature | 70.0 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ E111G | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| Stylac™ T8701 | Asahi Kasei Chemicals Corporation | AS | Stylac™ |
| Moplen EP548T | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| CYCOLOY™ CY2010 resin | SABIC Innovative Plastics Europe | PC+ABS | CYCOLOY™ |
| Huafon JF-W-6080 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |