LNP™ THERMOCOMP™ DF006ER compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cq4TzZ_LNP-THERMOCOMP-DF006ER-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* DF006ER is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release. Also known as: LNP* THERMOCOMP* Compound DF-1006 EM MR Product reorder name: DF006ER |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.43 | g/cm³ | ASTM D792 |
| -- | 1.42 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.48 | % | ISO 294-4 |
| Flow : 24 hr | 0.11 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9510 | MPa | ASTM D638 |
| -- | 7510 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 133 | MPa | ASTM D638 |
| Break | 106 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.7 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8760 | MPa | ASTM D790 |
| -- | 8500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 206 | MPa | ASTM D790 |
| -- | 197 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 870 | J/m | ASTM D4812 |
| 23°C 3 | 61 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.20 | J | ASTM D3763 |
| -- | 4.25 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 137 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 138 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 AT-1001 L | RTP Company | PPA | RTP |
| ADDINYL B2H V25 | ADDIPLAST | Nylon 6 | ADDINYL |
| Karina IVORY PVC COMPOUND 70900-35/ 1-J-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LOTTMER HS-170AB | Lotte Chemical Corporation | TPE | LOTTMER |
| DURANEX® CTN7133N/B | Polyplastics Co., Ltd. | PBT | DURANEX® |