IROGRAN® PS455-200
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CpsLgP_IROGRAN-PS455-200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN PS455-200 is a polyester based thermoplastic polyurethane intended for extrusion applications. IROGRAN PS455-200 is part of the HUNTSMAN film and sheet product range and offers a specially designed, flexible material with a broad processing window particularly suitable for film and sheet, textile laminations, and compounding. PERFORMANCE FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.19 | g/cm³ | ASTM D792, DIN 53478 |
| Melt Volume-Flow Rate (MVR) (177°C/2.16 kg) | 8.00 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Injection Molded) | 78 | ASTM D2240, DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | |||
| -- | 51 | mm³ | ASTM D395 |
| -- | 50 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| TMA 3 | Internal method | ||
| High : 635.0 µm | 130 | °C | Internal method |
| Low : 635.0 µm | 110 | °C | Internal method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 4 | |||
| 100% strain, 0.635mm | 2.34 | MPa | ASTM D412 |
| 100% strain, 0.635mm | 2.00 | MPa | DIN 53504 |
| 300% strain, 0.635mm | 4.83 | MPa | ASTM D412 |
| 300% strain, 0.635mm | 5.00 | MPa | DIN 53504 |
| Tensile Strength 5 | |||
| Fracture, 0.635mm | 41.4 | MPa | ASTM D412 |
| Fracture, 0.635mm | 42.0 | MPa | DIN 53504 |
| Tensile Elongation 6(Break, 0.635 mm) | 700 | % | ASTM D412, DIN 53504 |
| Tear Strength 7 | |||
| 0.635 mm | 66.5 | kN/m | ASTM D624 |
| 0.635 mm | 72 | kN/m | DIN 53515 |
| Compression Set 8 | ASTM D395, DIN 53517 | ||
| 23°C, 70 hr | 40 | % | ASTM D395, DIN 53517 |
| 70°C, 24 hr | 90 | % | ASTM D395, DIN 53517 |
| Bayshore Resilience 9 | 50 | % | ASTM D2632 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 50.0 - 60.0 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 140 | °C | |
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 150 | °C | |
| Cylinder Zone 4 Temp. | 150 | °C | |
| Cylinder Zone 5 Temp. | 150 | °C | |
| Adapter Temperature | 150 | °C | |
| Die Temperature | 150 | °C |
| Extrusion instructions |
|---|
| Dew Point: -22°F |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Extruded Film |
| 4 . | Extruded Film |
| 5 . | Extruded Film |
| 6 . | Extruded Film |
| 7 . | Extruded Film |
| 8 . | Injection Molded |
| 9 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC MPH 62/D | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Lucky Enpla LGF1150 | Lucky Enpla Co LTD | PC | Lucky Enpla |
| Therma-Tech™ TT6600-5001-8 EC Grey | PolyOne Corporation | Nylon 66 | Therma-Tech™ |
| Cellidor CP 300-18 | ALBIS PLASTIC GmbH | CAP | Cellidor |
| POTICON NT962 | Otsuka Chemical Co., Ltd. | Nylon, Unspecified | POTICON |