Latamid 66 H2 G/25-V0KB4
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cmwkx2_Latamid-66-H2-G-25-V0KB4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on Polyamide 66 (PA 66). Heat stabilised. Glass fibres. UL94 V-0 classified, with red phosphorous. Product UL certified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.1 to 1.3 | % | |
| Flow : 2.00 mm | 0.40 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 6800 | MPa | |
| 60°C | 4700 | MPa | |
| 90°C | 2800 | MPa | |
| 120°C | 2300 | MPa | |
| 150°C | 2000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 60°C | 70.0 | MPa | |
| Yield, 90°C | 50.0 | MPa | |
| Yield, 120°C | 40.0 | MPa | |
| Yield, 150°C | 35.0 | MPa | |
| Break, 23°C | 110 | MPa | |
| Break, 60°C | 70.0 | MPa | |
| Break, 90°C | 50.0 | MPa | |
| Break, 120°C | 40.0 | MPa | |
| Break, 150°C | 35.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 60°C | 3.5 | % | |
| Yield, 90°C | 5.0 | % | |
| Yield, 120°C | 5.0 | % | |
| Yield, 150°C | 4.8 | % | |
| Break, 23°C | 2.2 | % | |
| Break, 60°C | 4.0 | % | |
| Break, 90°C | 6.0 | % | |
| Break, 120°C | 6.0 | % | |
| Break, 150°C | 5.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 50 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Notched Izod Impact | ASTM D256A | ||
| -20°C, 3.20 mm | 70 | J/m | |
| 23°C, 3.20 mm | 100 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 125 | °C | |
| Vicat Softening Temperature | 240 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | |
| 2.00 mm | 800 | °C | |
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® B3EG6 BK00564 | BASF Corporation | Nylon 6 | Ultramid® |
| UNITIKA Nylon 66 A175G15 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| ARCEL® ULV (4.00 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| Jianqiao PPGF30 | Shanghai Jianqiao Plastic Co., Ltd. | PP, Unspecified | Jianqiao |
| NHU-PPS 1H30C | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |