Generic PP, Unspecified - Calcium Carbonate
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cmqi9z_Generic-PP-Unspecified---Calcium-Carbonate.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Calcium Carbonate This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.953 - 1.27 | g/cm³ | ASTM D792 |
| 23°C | 0.980 - 1.36 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.5 - 27 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 1.0 - 1.6 | % | ASTM D955 |
| Transverse flow : 23°C | 1.7 - 1.9 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 85 - 99 | ASTM D785 | |
| Durometer Hardness (23°C) | 66 - 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1720 - 3100 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 15.2 - 30.5 | MPa | ASTM D638 |
| 23°C | 20.8 - 26.6 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 9.8 - 10 | % | ASTM D638 |
| Fracture, 23°C | 3.0 - 200 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1140 - 2840 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 26.4 - 51.7 | MPa | ASTM D790 |
| Yield, 23°C | 29.8 - 48.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 25 - 99 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 520 - 1600 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 1.87 - 29.0 | J | ASTM D3029 |
| Dart Drop Impact (23°C) | 2.26 - 32.8 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 84.0 - 122 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 50.2 - 68.5 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.3 - 94.1 | °C | |
| Drying Time | 1.5 - 3.0 | hr | |
| Rear Temperature | 202 - 211 | °C | |
| Middle Temperature | 207 - 208 | °C | |
| Front Temperature | 210 - 213 | °C | |
| Nozzle Temperature | 215 - 218 | °C | |
| Processing (Melt) Temp | 209 - 241 | °C | |
| Mold Temperature | 37.2 - 53.1 | °C | |
| Injection Pressure | 6.55 - 86.5 | MPa | |
| Holding Pressure | 5.17 - 7.20 | MPa | |
| Back Pressure | 0.241 - 0.694 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified - Calcium CarbonateThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 1040EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced TPO | POLYTROPE® |
| Royalite R12 | Spartech Plastics | ABS | Royalite |
| Vital-Line SHM1332 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Vital-Line |
| Globalene® ST861 | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |
| LNP™ LUBRICOMP™ DFP32 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |