Genestar™ G1302
| Category: | Nylon 9T , Polyamide 9T |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | Genestar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CmVzGx_Genestar-G1302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The G1300H and G1350H are suitable for use in a wide range of electrical and electronics components as UL94 HB flammability rating, while the G1302 grade delivers low friction. HB grades do not contain halogen-containing flame-retardants. The GW1458HF offers low warpage and high flow-ability. *'Halogen free' follows the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (320°C/2.16 kg) | 46 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 1.00 mm | 0.20 | % | |
| Across Flow : 1.00 mm | 0.70 | % | |
| Water Absorption 1(Equilibrium, 40°C, 95%RH) | 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 165 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 9000 | MPa | ASTM D790 |
| Flexural Strength | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 290 | °C | ASTM D648 |
| Glass Transition Temperature | 125 | °C | |
| Melting Temperature | 306 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Dielectric Constant (10.0 GHz) | 3.30 | ASTM D150 | |
| Dissipation Factor (10.0 GHz) | 9.0E-3 | ASTM D150 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 2(320°C, 500.0 µm) | 5.50 | cm | |
| Weld Elongation | 0.70 | % | ASTM D638 |
| Weld Strength | 47.0 | MPa | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | 96 hrs |
| 2 . | 750kgf |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® 42LH-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Nypol® PA A3 Z40 HS NTLA010 NR457 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| APEX® 90-A481R-80-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Ateva® 1241 | Celanese EVA Performance Polymers | EVA | Ateva® |
| Lupoy® HG5000B | LG Chem Ltd. | PC+ABS | Lupoy® |