ACRYPET® VR L40
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Mitsubishi Rayon Co., Ltd. |
| Trademark: | ACRYPET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cm5r0g_ACRYPET-VR-L40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Acrypet®VR L40 is a polymethyl methacrylate-acrylic material,. This product is available in North America,. Acrypet®The main features of VR L40 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 67 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 42.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 80 | % | ASTM D638 |
| Flexural Modulus (6.35 mm) | 1960 | MPa | ASTM D790 |
| Flexural Strength (6.35 mm) | 62.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 94.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 109 | °C | ASTM D1525 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance (3200 µm) | 92.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Surface Resistivity, JIS K6911: >10^16 ohmVolume Resistivity, JIS K6911: >10^15 ohm-cmDielectric Breakdown Strength: 15 kV/mmDielectric Constant, 60Hz: 3.9Dielectric Loss Tangent, 60Hz: 0.04Arc Resistance, JIS K6911: No Trace |
| Note Message | |
|---|---|
| 1 . | Type 1 |
| 2 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 282 AR 15 TFE 15 | RTP Company | Nylon 66 | RTP |
| Spartech Polycom SC7-7010RF | Spartech Polycom | PC | Spartech |
| TYNELOY® CE4200 | Tyne Plastics LLC. | PC+PET | TYNELOY® |
| Lion Idemitsu Composites PPS C-719SG | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Karina BLACK PVC COMPOUND 750-48/1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |