Alathon® ETP H4745
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® ETP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cm4nSH_Alathon-ETP-H4745.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON H 4745 is a multi-purpose, high-flow resin featuring enhanced cold temperature impact performance, enhanced processability and thermal stability for fast cycling and exhibits good color and organoleptic properties. Typical applications are cultured dairy containers, margarine containers, butter tubs and promotional drink cups. Freezer applications include ice cream, sherbet and other frozen dessert containers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.946 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.59 to 0.63 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 45 | g/10 min | ASTM D1238 |
| Spiral Flow | 48.8 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 724 | MPa | |
| 1% Secant | 609 | MPa | |
| Tensile Strength 2(Break) | 24.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 6.3 | % | ASTM D638 |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 965 | MPa | |
| 1% Secant | 979 | MPa | |
| 2% Secant | 765 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | 24 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 63.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 |
| Peak Melting Temperature | 112 to 126 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP548N | LyondellBasell Industries | PP Homopolymer | Moplen |
| PLUSTEK RA303G4 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| POLYfill PPC TS4030 H | Polykemi AB | PP Copolymer | POLYfill |
| Sylvin 8200-85 Black 293 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Jam HD-52505/UV | Jam Petrochemical Company | HDPE | Jam |