LNP™ THERMOTUF™ V1000 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ClmVoc_LNP-THERMOTUF-V1000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF* V1000 is a compound based on unfilled Super Tough Nylon resin. Added feature of this material is: High Impact. Also known as: LNP* THERMOTUF* Compound V-1000 Product reorder name: V1000 |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.3 to 1.5 | % | |
| Across Flow : 24 hr | 1.3 to 1.5 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.80 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.4 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1930 | MPa | ASTM D638 |
| -- | 1800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 45.1 | MPa | ASTM D638 |
| Yield | 44.0 | MPa | ISO 527-2 |
| Break | 50.6 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.6 | % | ASTM D638 |
| Yield | 17 | % | ISO 527-2 |
| Break | 60 | % | ASTM D638 |
| Break | 170 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1930 | MPa | ASTM D790 |
| -- | 1700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 74.7 | MPa | ASTM D790 |
| -- | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 84 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 140 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 56.9 | J | ASTM D3763 |
| -- | 77.3 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 53.3 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 56.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.3E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.3E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 271 to 282 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 48.9 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 10 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR5-2015 | Spartech Polycom | PP Copolymer | Spartech |
| Nypol® PA B3 G30 PRTA011 NT303 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| IPC PP 4830C-C | International Polymers Corporation | PP Copolymer | IPC PP |
| Karina WHITE COLOR CONCENTRATE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLIMAXX 2311LCXGA4 | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |