Amilan® CM2001
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ClUg8q_Amilan-CM2001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Amilan® CM2001 is a Polyamide 610 (Nylon 610) product. It is available in Asia Pacific, Europe, or North America. |
| General Information | |
|---|---|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.08 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | Internal Method | |||
| 1.00 mm 1 | 0.30 to 0.70 | -- | % | |
| 3.00 mm 2 | 0.70 to 1.3 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.30 | -- | % | |
| Saturation, 23°C | 4.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 116 | -- | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 85.0 | -- | MPa | |
| 23°C | 55.0 | 40.0 | MPa | |
| 80°C | 25.0 | -- | MPa | |
| Tensile Strain (Break, 23°C) | 50 | 50 | % | ISO 527-2 |
| Flexural Modulus | ISO 178 | |||
| -40°C | 2300 | -- | MPa | |
| 23°C | 2000 | 900 | MPa | |
| 80°C | 500 | -- | MPa | |
| Flexural Stress (23°C) | 95.0 | 55.0 | MPa | ISO 178 |
| Compressive Stress (23°C) | 65.0 | -- | MPa | ISO 604 |
| Shear Strength (23°C) | 50.0 | 45.0 | MPa | ASTM D732 |
| Taber Abrasion Resistance (1000 Cycles) | 4.00 | -- | mg | ISO 9352 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 40 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 180 | -- | °C | ISO 75-2/B |
| Melting Temperature | 225 | -- | °C | DSC |
| CLTE - Flow | 1.2E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1900 | -- | J/kg/°C | |
| Thermal Conductivity | 0.25 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+13 to 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Dielectric Constant 3 | IEC 60250 | |||
| 23°C, 50 Hz | 3.90 | -- | ||
| 23°C, 1 kHz | 3.60 | -- | ||
| 23°C, 1 MHz | 3.10 | -- | ||
| Dissipation Factor 4 | IEC 60250 | |||
| 23°C, 50 Hz | 0.040 | -- | ||
| 23°C, 1 kHz | 0.040 | -- | ||
| 23°C, 1 MHz | 0.020 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability | Self-Extinguishing | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x1mm |
| 2 . | 80x80x3mm |
| 3 . | 60% RH |
| 4 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3755 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP 4799 X 115376 C | RTP Company | PTT | RTP |
| Hostalen CRP 100 RESIST CR black | LyondellBasell Industries | HDPE | Hostalen |
| INELEC PSUCF10 | Infinity LTL Engineered Compounds | PSU | INELEC |
| Pinnacle PP 1703 | Pinnacle Polymers | PP Homopolymer | Pinnacle PP |