TOTAL Polyethylene Lotrène® Q2018 C
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CkcEwI_TOTAL-Polyethylene-Lotr-ne-Q2018-C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lotrène ® Q2018 C is an ethylene-butene copolymer produced in a gas phase reactor. It is designed for delivering competitive performance in most cast film applications. Lotrène ® Q2018 C can be processed at high output rates with moderate extrusion pressure, good bubble stability and gauge control on cast film machine designed for LLDPE. Lotrène ® Q2018 C can advantageously be blended with LDPE or other PE resins used in blown film mono extrusion or coextrusion to improve film properties. Lotrène ® Q2018 C is suited for many applications in the field of consumer, industrial, food or hygiene packaging as well as stretch film and non-packaging applications like agricultural films e.g. mulching films. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Modulus | ISO 178 | ||
| 1% secant, MD : 20 µm, cast film | 165 | MPa | ISO 178 |
| 1% secant, TD : 20 µm, cast film | 170 | MPa | ISO 178 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm, cast film | 9.70 | MPa | ISO 527-3 |
| TD : Yield, 20 µm, cast film | 9.60 | MPa | ISO 527-3 |
| MD : Fracture, 20 µm, cast film | 37.0 | MPa | ISO 527-3 |
| TD : Fracture, 20 µm, cast film | 23.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 20 µm, cast film | 330 | % | ISO 527-3 |
| TD : Fracture, 20 µm, cast film | 670 | % | ISO 527-3 |
| Dart Drop Impact 1(20 µm, Cast Film) | 35 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 20.0 µm | 12.0 | kN/m | ISO 6383-2 |
| TD : 20.0 µm | 193.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 2 | 100 | °C | ASTM D1525 |
| Melting Temperature | 121 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 92 | ASTM D2457 | |
| Haze (20.0 µm, Cast Film) | 1.8 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 250 | °C |
| Extrusion instructions |
|---|
| Line speed: > 400 m/minDie gap: > 0.8 mmFilm properties are measured on cast line with following parameters: 30 mm screw diameter, L/D = 30:1, die length = 600 mm, die gap = 0.8 mm, line speed = 50 m/min, temperature setting = 180-230°C. Melt temperature = 250 °C and Chill roll temperature = 25 °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | A120 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ALC-72D-B20 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| TEKNIFLEX® VA760 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PCTFE | TEKNIFLEX® |
| EPDM 785 | The Dow Chemical Company | EPDM | EPDM |
| ADVANCENE™ bEE-4909-AAH | ETHYDCO | HDPE, HMW | ADVANCENE™ |
| Elastofoam® 38100R / 3120T | BASF Corporation | PUR, Unspecified | Elastofoam® |