Polytron® P50B07/P50B07-S (Single Strand)
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | Polytron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ck0T3h_Polytron-P50B07-P50B07-S-Single-Strand-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A chemically coupled 50% LGF reinforced black PP, heat stabilized, UV stabilized for injection moulding applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.20 to 0.30 | % | |
| -- | 0.20 to 0.30 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12900 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 135 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 1.7 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 11000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 210 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 22 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 250 | J/m | ASTM D256 |
| 23°C | 25 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 159 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 167 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Flammability | 20 | mm/min | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2285 LF | RTP Company | PEEK | RTP |
| SAXAMID™ 126F4RZ21 | SAX Polymers | Nylon 6 | SAXAMID™ |
| Vipel® F701-FBB-15 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| LUVOCOM® 1850-7784 | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| LNP™ THERMOCOMP™ QC006 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |