Braskem PE STS7006
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem America Inc. |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cissc3_Braskem-PE-STS7006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: STS7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a great combination among mechanical, optical and stiffness properties. Besides STS7006 has low gels content which ensure a production of excellent appearance films. This product is identified as PE 114 according to ASTM D-4976-04a standard specification. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Additives: Antiblocking. Slip agent. Applications: High clarity films for coextruded food packaging, such as: cheese, meat, sausages, sliced ham, etc. Process: Blown Film Extrusion. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 50 µm, blown film | 140 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm, blown film | 170 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 25.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 350 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 700 | % | ASTM D882 |
| Dart Drop Impact 1(50 µm, Blown Film) | 170 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 310 | g | ASTM D1922 |
| TD : 50 µm, blown film | 250 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45, blown film | 60 | ASTM D2457 | |
| 60, blown film | 84 | ASTM D2457 | |
| Haze (Blown Film) | 9.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 95 | % | ASTM D6866 |
| Blown Film Properties: 50µm thickness film, processed in a 50mm blow film line with barrier screw. 25:1 L/D and a 1.0 mm die gap at a 2.3: 1 blow up ratio.Recommended processing conditions:Blow Film ExtrusionTemperature Profile:……....from 150 to 185°CMass Temperature:........... from 180 to 185°CBlow up Ratio:…………….….from 2,0 to 3,0:1Die Gap:………………………..1,0 mm |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP6415 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME Specialty PS |
| Chemlon® 233 GV | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| COPYLENE® CH020-01 | Phillips 66 | PP Homopolymer | COPYLENE® |
| Globalprene® 9554U | Lee Chang Yung Chemical Industry Corp. | SEBS | Globalprene® |
| KYOCERA KE-1150 | KYOCERA Chemical Corporation | Epoxy | KYOCERA |