Eraclene® BC 82
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Eraclene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CiEHMD_Eraclene-BC-82.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eraclene BC 82 is a high density polyethylene resin (HDPE), with antioxidants, suitable for blow moulding application. It is especially recommended for the production of containers up to 20 liters. Eraclene BC 82 combines a good stress cracking resistance with a good rigidity and impact strength. This resin exhibits a high melt strength together with a moderate swelling. Eraclene BC 82 is characterized by an intermediate molecular weight distribution which balances overall performances with ease of processing. Main Application Eraclene BC 82 is used to produce, with high-speed machines, blow moulded containers for household and industrial chemicals (detergents, bleaches, etc), cosmetics (shampoos, creams, lotions, etc.), health and medical aids. Eraclene BC 82 is suitable for thin wall items and can be extruded into profiles and sheets. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.25 | g/10 min | |
| 190°C/5.0 kg | 0.90 | g/10 min | |
| Environmental Stress-Cracking Resistance (Compression Molded) | > 60.0 | hr | ISO 22088 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 27.0 | MPa | |
| Break, Compression Molded | 30.0 | MPa | |
| Tensile Strain (Break, Compression Molded) | > 600 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 1200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(Compression Molded) | 180 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 125 | °C | ISO 306/A |
| Melting Temperature | 135 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC LLDPE UF925 | Lotte Chemical Corporation | LLDPE | SEETEC LLDPE |
| Nanjing Hongrui PP P860 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| Novalloy-B B2706 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| LNP™ THERMOCOMP™ RX10408H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Lusin® Clean 1010 | Chem-Trend L.P. | TP, Unspecified | Lusin® |