MAJORIS HPS G400 - 8229
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ChMVGM_MAJORIS-HPS-G400---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS HPS G400 - 8229 is a 40 % glass fibre reinforced polyphenylene sulfide, intended for injection moulding. The product is available in black. They combine high mechanical, thermal and electrical properties with excellent chemical and oxidation resistance, lower shrinkage. This product is inherently flame retardant UL 94: V0. APPLICATIONS MAJORIS HPS G400 - 8229 is intended for the injection moulding of electrical components and automotive applications including interior, electrical and mechanical systems, such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.62 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.20 to 0.60 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 195 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 13000 | MPa | ISO 178 |
| Flexural Stress | 233 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 47 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 266 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 24 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 5.30 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 320 to 340 | °C | |
| Mold Temperature | 140 to 160 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNFROST® KD90EA | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNFROST® |
| Sylvin 8873-92 White 1196 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Trilliant™ HC HC3220-0030 RS Natural | PolyOne Corporation | PC | Trilliant™ HC |
| LG PVC LB100M | LG Chem Ltd. | PVC, Unspecified | LG PVC |
| Plenco 03356 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |