Halene H M5005L
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CgosMa_Halene-H-M5005L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
M5005L is a Narrow MWD HDPE produced by the Spherilene Technology. M5005L is ideally suited for injection molding of heavy-duty Crates & Industrial products. The precise control of morphology & MWD during polymerization confers superior processability and improved performance properties compared to conventional HDPE grades. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.950 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Spiral Flow 2 | 35.0 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Injection Molded) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 3 | ASTM D638 | ||
| Yield, Injection Molded | 25.0 | MPa | |
| Break, Injection Molded | 34.0 | MPa | |
| Tensile Elongation 4(Break, Injection Molded) | > 1000 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 850 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 100 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 78.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 5 |
| Peak Melting Temperature | 132 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 185 to 235 | °C | |
| Middle Temperature | 185 to 235 | °C | |
| Front Temperature | 185 to 235 | °C | |
| Nozzle Temperature | 235 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | Melt Temperature: 235°C |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BK10NT6510 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Mylar® EL (500 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| AMPLIFY™ GR 205 | The Dow Chemical Company | MAH-g | AMPLIFY™ GR |
| Karina IVORY PVC COMPOUND 105905-35/ 1-BY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MARPOL® Homo 13.F | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |