LNP™ LUBRICOMP™ RP004 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cg4qrw_LNPLUBRICOMPRP004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RP004 is a compound based on Nylon 66 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound RL-4540 Product reorder name: RP004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.9 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.9 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.9 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.9 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.80 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2760 | MPa | ASTM D638 |
| -- | 2730 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 5.52 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2 |
| Fracture | 60.7 | MPa | ASTM D638 |
| Fracture | 63.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 22 | % | ASTM D638 |
| Yield | 26 | % | ISO 527-2 |
| Fracture | 23 | % | ASTM D638 |
| Fracture | 27 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| Flexural Stress | 82.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.20 | ASTM D3702 Modified | |
| With Self-Static | 0.045 | ASTM D3702 Modified | |
| Wear Factor - Washer | 3.50 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 5.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 350 | J/m | ASTM D4812 |
| 23°C 3 | 89 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.70 | J | ASTM D3763 |
| -- | 1.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 237 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 200 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 63.3 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 63.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 9.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 8.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.4E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA66 FRPA66 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 66 | Shandong PA66 |
| TRANSMARE® 35HGF30-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| 4MID® 9B20000 | 4Plas | Nylon 6 | 4MID® |
| Gallonprene® GP520-8511 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 8271 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |