INSTRUC PPGB30
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INSTRUC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cg2tga_INSTRUC-PPGB30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS BEAD FILLED POLYPROPYLENE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.1 to 1.6 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 24.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256 |
| Unnotched Izod Impact | 430 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 68.3 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+17 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 227 | °C | |
| Mold Temperature | 37.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.013 to 0.025 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEOPLAST 180 FT EB | Zylog Plastalloys | TPV | NEOPLAST |
| Geon™ Vinyl Rigid Extrusion 87556 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| KYOCERA KE-G240V | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| PAXOTHENE® NA208 | USI Corporation | LDPE | PAXOTHENE® |
| Plaslube® PA6/6 GF30 TL15 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |