ALCOM® PA6 900/1 GF30 WT1165-10LB
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CdnAa4_ALCOM-PA6-900-1-GF30-WT1165-10LB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM® PA6 900/1 GF30 WT1165-10LB is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Applications of ALCOM® PA6 900/1 GF30 WT1165-10LB include automotive, handles, lighting applications and reflectors. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Moisture - Karl Fischer | 0.10 | % | ISO 15512 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tristimulus Value | |||
| Y10 of Reflection | 0.0 | % | DIN 5033 |
| Y10 of Transmittance : 500.0 µm | 1.7 | % | ISO 13468 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 196 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 122 | MPa | |
| -- | 123 | MPa | |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 8700 | MPa | ISO 178 |
| Flexural Stress | 185 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 6.0 | kJ/m² | |
| -40°C | 4.0 | kJ/m² | |
| -20°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | 39 | kJ/m² | |
| -40°C | 36 | kJ/m² | |
| -20°C | 37 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 12 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 7000 | Colorite Polymers | PVC, Unspecified | Unichem |
| Nipol® NBR N1201L | Zeon Corporation | NBR | Nipol® NBR |
| Crastin® HR5315HF BK503 | DuPont Performance Polymers | PBT | Crastin® |
| EVALENE® PP PHY0221 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| Ferro PP CPP30GF39BK | Ferro Corporation | PP Homopolymer | Ferro PP |