Stanyl® TW271F8

Category: Nylon 46 , Polyamide 46
Manufacturer: DSM Engineering Plastics
Trademark: Stanyl®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: Cdduyk_Stanyl-TW271F8.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Stanyl® TW271F8 is a Polyamide 46 (Nylon 46) material filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America.

Important attributes of Stanyl® TW271F8 are:
  • Heat Stabilizer
  • Wear Resistant
General Information
Filler / Reinforcement
  • Glass Fiber, 40% Filler by Weight
Additive
  • Heat Stabilizer
Features
  • Good Wear Resistance
  • Heat Stabilized
  • Low Friction
PhysicalNominal ValueUnitTest Method
Density 1.63g/cm³ISO 1183
MechanicalNominal ValueUnitTest Method
Tensile Modulus 13000MPaISO 527-2
Tensile Stress (Break)210MPaISO 527-2
Tensile Strain (Break)3.0%ISO 527-2
Flexural Modulus 11500MPaISO 178
ImpactNominal ValueUnitTest Method
Charpy Notched Impact Strength (23°C)14kJ/m²ISO 179/1eA
Notched Izod Impact Strength (23°C)14kJ/m²ISO 180/1A
ThermalNominal ValueUnitTest Method
Heat Deflection Temperature (1.8 MPa, Unannealed)285°CISO 75-2/A
Melting Temperature 290°CISO 11357-3
InjectionNominal ValueUnit
Drying Temperature 80.0°C
Drying Time 4.0 to 8.0hr
Rear Temperature 280 to 320°C
Middle Temperature 300 to 320°C
Front Temperature 300 to 320°C
Nozzle Temperature 300 to 320°C
Processing (Melt) Temp 305 to 320°C
Mold Temperature 80.0 to 120°C
Injection Rate Moderate-Fast
Back Pressure 2.00 to 10.0MPa
Screw Compression Ratio 2.5:1.0
Resin Grade Manufacturer Category Trademark
SCANAMID 66 A13^ FX30 Polykemi AB Nylon 66 SCANAMID 66
SHIN-A SE-80P SHIN-A T&C Epoxy SHIN-A
SureSpec GS-025 Genesis Polymers PS (GPPS) SureSpec
Eastar™ BR003, Natural Eastman Chemical Company Copolyester Eastar™
LEXAN™ HPS6 resin SABIC Innovative Plastics PC LEXAN™