Laramid G/15
| Category: | PPA , Polyphthalamide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laramid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cdbr0C_Laramid-G-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Semi-aromatic polyammide. Glass fibres. Very good thermal properties. Good chemical resistance. Low moisture absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.85 to 1.2 | % | |
| Flow : 2.00 mm | 0.40 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C, Compression Molded | 7200 | MPa | |
| 60°C | 6800 | MPa | |
| 90°C | 5700 | MPa | |
| 120°C | 4400 | MPa | |
| 150°C | 2000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 120°C | 80.0 | MPa | |
| Yield, 150°C | 55.0 | MPa | |
| Break, 23°C | 110 | MPa | |
| Break, 60°C | 105 | MPa | |
| Break, 90°C | 100 | MPa | |
| Break, 120°C | 75.0 | MPa | |
| Break, 150°C | 55.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 120°C | 3.5 | % | |
| Yield, 150°C | 10 | % | |
| Break, 23°C | 2.0 | % | |
| Break, 60°C | 2.0 | % | |
| Break, 90°C | 2.0 | % | |
| Break, 120°C | 5.0 | % | |
| Break, 150°C | 12 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 17 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 40 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 280 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 125 | °C | |
| Vicat Softening Temperature | 265 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 310 to 330 | °C | |
| Mold Temperature | 150 to 170 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN GRP-353C | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| TOTAL Polyethylene MDPE 3802 B (Wire and Cable) | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| Nanjing Hongrui PBT T401 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| INSTRUC PEEKGF30HF | Infinity LTL Engineered Compounds | PEEK | INSTRUC |
| LG PVC LS100 | LG Chem Ltd. | PVC, Unspecified | LG PVC |