ENGAGE™ 7387 EL
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cc5HtI_ENGAGE-7387-EL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 7387 EL Polyolefin Elastomer is a revolutionary butene copolymer with higher molecular weight, better toughness, and higher melt strength than other commercially available polyolefin elastomers. It is well suited for extruded applications such as Wire & Cable. Main Characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.870 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | < 0.50 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 51 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, Compression Molded | 74 | ||
| Shore D, Compression Molded | 22 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 2.60 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 5.20 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 500 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 10.9 | MPa | |
| 2% Secant : Compression Molded | 11.3 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 38.0 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -52.0 | °C | Internal Method |
| Vicat Softening Temperature | 47.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 51.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 37.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ WCD944 resin | SABIC Innovative Plastics Europe | PPE+TPE | NORYL™ |
| Emulprene® 1778R | INSA | SBR, Emulsion | Emulprene® |
| EPO-TEK® T905BN-3 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| POFEX EP8300S 95A/95C | POLYROCKS CHEMICAL CO., LTD | TPU, Unspecified | POFEX |
| Alpha PVC 2222RX-75 | Mexichem Specialty Compounds Inc. | PVC, Unspecified | Alpha PVC |