RTP 3483-4

Category: LCP , Liquid Crystal Polymer
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: CbdwEZ_RTP-3483-4.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Carbon Fiber
General Information
Filler / Reinforcement
  • Carbon fiber reinforced material, 20% filler by weight
RoHS Compliance
  • Contact manufacturer
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.39g/cm³ASTM D792
Molding Shrinkage - Flow (3.20 mm)0.050%ASTM D955
MechanicalNominal ValueUnitTest Method
Tensile Modulus 27600MPaASTM D638
Tensile Strength 152MPaASTM D638
Tensile Elongation (Yield)1.0%ASTM D638
Flexural Modulus 20000MPaASTM D790
Flexural Strength 200MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.20 mm)59J/mASTM D256
Unnotched Izod Impact (3.20 mm)370J/mASTM D4812
Additional InformationNominal ValueUnit
Primary Additive 20%
InjectionNominal ValueUnit
Drying Temperature 149°C
Drying Time 8.0hr
Dew Point -28.9°C
Processing (Melt) Temp 363 - 399°C
Mold Temperature 65.6 - 93.3°C
Injection Pressure 68.9 - 124MPa
Injection instructions
The key to successfully molding this material is to start mold open cycles as soon as the screw reaches its retracted position.
Resin Grade Manufacturer Category Trademark
SABIC® PPcompound 55T1040 SABIC Innovative Plastics PP, Unspecified SABIC® PPcompound
Biocycle 189C-1 Biocycle Biodeg Polymers Biocycle
Evoprene™ COGEE 638 AlphaGary SEBS Evoprene™ COGEE
Hanwha Total PP RB83T HANWHA TOTAL PETROCHEMICALS Co., Ltd. PP, Unspecified Hanwha Total PP
LNP™ THERMOCOMP™ ZX08309 compound SABIC Innovative Plastics Asia Pacific PPE+PS LNP™ THERMOCOMP™