NYLOY® NG-1035NM
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nytex Composites Co., Ltd. |
| Trademark: | NYLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CZmxoO_NYLOY-NG-1035NM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NYLOY® NG-1035NM is a Polyamide 6 (Nylon 6) material filled with 35% glass fiber. It is available in Asia Pacific or North America for injection molding. Primary attribute of NYLOY® NG-1035NM: Impact Modified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 | g/cm³ | ASTM D792 |
| -- | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow | 0.34 | % | |
| Across Flow | 0.96 | % | |
| Ash Content | 35 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 115 | ASTM D785 | |
| R-Scale | 114 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 152 | MPa | ASTM D638 |
| -- | 140 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 4.7 | % | ASTM D638 |
| Break | 3.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8290 | MPa | ASTM D790 |
| -- | 7500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 225 | MPa | ASTM D790 |
| -- | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 27 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 207 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 1206 LD | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| RTP 3583 | RTP Company | FEP | RTP |
| ACCUTECH™ HP0334W10L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| BMC 3001 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| POFEX EP8004S150F | POLYROCKS CHEMICAL CO., LTD | XLPE | POFEX |