| Jackdaw PLA HS10VN6611 is a Polylactic Acid (PLA) product. It can be processed by extrusion and is available in Europe. Primary characteristic: eco-friendly/green. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield | 60.0 | MPa | ASTM D638, ISO 527-2 |
| Break | 48.0 | MPa | ISO 527-2 |
| -- | 48.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638, ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 1 | 23.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | 23 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 55.0 | °C | ASTM D648 |
| Peak Melting Temperature | 148 | °C | ASTM D2117, ISO 1218 |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYLEX™ X7509HP resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |
| Ultramid® B35G3 SI BK23216 | BASF Corporation | Nylon 6 | Ultramid® |
| ENVIROPLAS® ENV11-NC720 | ENVIROPLAS®, Inc. | PC | ENVIROPLAS® |
| HiFill® ABS GF20 BK | Techmer Engineered Solutions | ABS | HiFill® |
| LNP™ LUBRICOMP™ LX91475 compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |