LEXAN™ BPL1000 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CYggOx_LEXAN-BPL1000-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with UL-94 V0 rating at 0.8mm. LEXAN BPL1000 resin offers various opaque color options and is ideal for thin wall applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.17 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 23.2 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.50 to 0.70 | % | |
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 24 hr | 0.15 | % | ASTM D570 |
| Saturation, 23°C | 0.35 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2680 | MPa | ASTM D638 |
| -- | 2460 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 58.8 | MPa | Internal Method |
| Yield 3 | 63.4 | MPa | ASTM D638 |
| Yield | 64.8 | MPa | ISO 527-2/50 |
| Break 4 | 51.0 | MPa | ASTM D638 |
| Break | 53.5 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 4.8 | % | ASTM D638 |
| Yield | 4.7 | % | ISO 527-2/50 |
| Break | 100 | % | Internal Method |
| Break 6 | 96 | % | ASTM D638 |
| Break | 97 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 2670 | MPa | ASTM D790 |
| -- | 2200 | MPa | ASTM D790 |
| -- 8 | 2370 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 93.2 | MPa | ASTM D790 |
| -- | 94.8 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 102 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 600 | J/m | ASTM D256 |
| -30°C 11 | 12 | kJ/m² | ISO 180/1A |
| 23°C 12 | 18 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 48.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 106 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 96.1 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 111 | °C | ASTM D1525 14 |
| -- | 113 | °C | ISO 306/B50 |
| -- | 114 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : -30 to 30°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.60 mm, in Oil) | 27 | kV/mm | ASTM D149 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.00 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 2.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 0.030 | ||
| 60 Hz | 0.030 | ||
| 1 MHz | 0.010 | ||
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.450 mm | V-2 | ||
| 0.800 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 800 | °C | IEC 60695-2-13 |
| Oxygen Index | 36 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| 14 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1800 A FR UV | RTP Company | PC+Acrylic | RTP |
| Badaflex® TPE-S 80A 1000 | Bada AG | TPE | Badaflex® |
| Bynel® 4206 | DuPont Packaging & Industrial Polymers | LDPE | Bynel® |
| Europrene® SOL T 166 | Versalis S.p.A. | SBS | Europrene® |
| Lustran® ABS 446 | INEOS ABS (USA) | ABS | Lustran® ABS |