EMERGE™ PC 8410-10
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CYDXut_EMERGE-PC-8410-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 8410-10 advanced resin is a transparent, ignition resistant PC resin, also available in opaque colors, that contains no chlorinated or brominated or phosphorous based additives. The resin is designed to meet the German norm DIN VDE-0472/Part 815 on halogens. This resin combines good mechanical and high heat properties, maintains excellent processability and contains mold release agent. EMERGE™ PC 8410-10 advanced resin has a UL94 V0 rating at 1.8 mm. Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 60.0 | MPa | |
| Break | 58.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | |
| Break | > 100 | % | |
| Flexural Modulus | 2350 | MPa | ISO 178 |
| Flexural Stress | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C) | 70 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 144 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 141 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 143 | °C | ISO 306/B50 |
| Ball Indentation Temperature | > 130 | °C | IEC 60335-1 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 17 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 1 Hz | 2.70 | ||
| 50 Hz | 2.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 1 Hz | 1.0E-3 | ||
| 50 Hz | 1.0E-3 | ||
| Comparative Tracking Index (Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm 1 | V-2 | ||
| 1.50 mm 2 | V-2 | ||
| 1.80 mm | V-0 | ||
| 3.00 mm 3 | V-0 | ||
| Glow Wire Flammability Index 4 | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature 5 | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | |
| 2.00 mm | 800 | °C | |
| 3.00 mm | 800 | °C | |
| Oxygen Index 6 | 40 | % | ISO 4589-2 |
| Needle Flame Test 7(1.50 mm) | PASS | IEC 60695-2-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 87.0 to 91.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | > 300 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 6 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 7 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ NH5020 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Adell Polyamide AT-17 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Cellidor CP 410-11 | ALBIS PLASTIC GmbH | CAP | Cellidor |
| FORMEX® GK-62 | ITW FORMEX | PP, Unspecified | FORMEX® |
| Hanwha Total PP GB14 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |