Multi-Flex® TPE A8030 C2
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Multibase, A Dow Corning Company |
| Trademark: | Multi-Flex® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CXaGDp_Multi-Flex-TPE-A8030-C2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Multi-Flex® TPE A8030 C2 is a Thermoplastic Elastomer (TPE) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 124 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 3.10 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 380 | % | ASTM D412 |
| Tear Strength | 22.8 | kN/m | ASTM D624 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 182 | °C | |
| Middle Temperature | 191 | °C | |
| Front Temperature | 199 | °C | |
| Nozzle Temperature | 204 | °C | |
| Processing (Melt) Temp | 204 | °C | |
| Mold Temperature | 26.7 to 37.8 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoPrene 85A-4000 | KMI Group Inc. | TPV Alloy | PrimoPrene |
| TRISTAR® PC-10FR-(VIK) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| Cellophane™ K160HB20/23 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| LNP™ STAT-KON™ DE0069F compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| Plenco 01508 (Transfer) | Plastics Engineering Co. | Polyester, TS | Plenco |