Hostalen ACP 9240 Plus
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CSMOWf_Hostalen-ACP-9240-Plus.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen ACP 9240 Plus is a high density polyethylene characterised by superior toughness and stiffness. Hostalen ACP 9240 Plus can be converted on HDPE blown film equipment with a homogeneous appearance and very low gel level. The very good bubble stability permits the production of wrinkle free and flat films within a wide range of blow up ratios. Typical applications are carrier and meat bags, inliners for drums, paper bags and FIBC as well as heavy duty bags. Foodlaw compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.946 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 6.0 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.20 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Film Thickness - Recommended / Available | 10 to 200 µm | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 20 µm, blown film | 80.0 | MPa | ISO 527-3 |
| TD : 20 µm, blown film | 65.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 20 µm, blown film | 400 | % | ISO 527-3 |
| TD : Broken, 20 µm, blown film | 540 | % | ISO 527-3 |
| Dart Drop Impact (20 µm, Blown Film) | > 300 | g | ASTM D1709 |
| Additional Information |
|---|
| Film properties tested using 20 µm thickness blown film extruded at a melt temperature of 220°C, long stalk process, blow-up ratio 4:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Methylon 75202 | Durez Corporation | Phenolic | Methylon |
| WPP PP PRC25TF2HFL-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Glastherm® HT | Glastic Corporation | Polyester, TS | Glastherm® |
| Hyundai EP PA6 LS240 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| CYCOLAC™ MG29 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |