DENIFORM 2010
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Vamp Tech |
| Trademark: | DENIFORM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CRpYzQ_DENIFORM-2010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POM, 20% glass fiber reinforced, not Flame Retardant compound, good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Water Absorption (Saturation) | 0.80 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 70.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 4.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 155 | °C | ASTM D1525 1 |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI Str | 90.0 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 190 | °C | |
| Mold Temperature | 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G25 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| WPP TPO TPO-2505 P Black | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| Zythane® 7070A | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| ADPOLY EM-510M | Lotte Chemical Corporation | LLDPE | ADPOLY |
| Arnitel® PL460-S | DSM Engineering Plastics | TPC-ET | Arnitel® |