Borealis PP RA7050-GN
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CRDzzG_Borealis-PP-RA7050-GN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PP-RCT (PolyPropylene-Random Crystallinity Temperature) is a material classification defined in ISO 1043-1:2001 to describe the second-generation class of PP-R materials. This pipe class, PP-RCT, has recently been included in EN ISO 15874, the global standard for plastics piping systems for Hot and Cold Water pipe installations and enable increased performance and competitiveness for pipe producers. RA7050-GN is a PP-RCT polypropylene-random-copolymer with a special crystallinity brought about by a special beta-nucleation which exhibits an improved pressure resistance, especially at elevated temperatures. PP-RCT materials such as RA7050-GN are designed to fulfil the PP-RCT pipe class as described in the EN ISO 15874 standard, e.g. 50 years service life at 70°C at 5 MPa, compared to 3.2 MPa for standard PP-R materials when tested according to the ISO 9080 pipe pressure tests. RA7050-GN is ready compounded for maximum quality control. The colour of RA7050-GN is green similar to RAL 6024. Applications In general RA7050-GN is intended to be used in applications for plumbing and heating, such as in-house hot and cold water pipes and fittings, floor and wall heating systems and radiator connections. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.25 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, Injection Molded) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, Injection Molded) | 10 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C, injection molding | 2.0 | kJ/m² | ISO 179/1eA |
| 0°C, injection molding | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 40 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (0 to 70°C) | 1.5E-4 | cm/cm/°C | DIN 53752 |
| Thermal Conductivity | 0.24 | W/m/K | DIN 52612 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 200 | °C | |
| Nozzle Temperature | 220 - 250 | °C | |
| Processing (Melt) Temp | < 250 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 215 - 230 | °C | |
| Cylinder Zone 2 Temp. | 215 - 230 | °C | |
| Cylinder Zone 3 Temp. | 215 - 230 | °C | |
| Cylinder Zone 4 Temp. | 215 - 230 | °C | |
| Cylinder Zone 5 Temp. | 215 - 230 | °C | |
| Adapter Temperature | 220 - 230 | °C | |
| Melt Temperature | 220 - 230 | °C | |
| Die Temperature | 220 - 230 | °C |
| Extrusion instructions |
|---|
| Screen pack: sieve 60 to 100 mesh |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TULAMID® PA-SV30-L1 | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| UBE Polyethylene J2522 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Akulon® K224-LG6 /E | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Karina BLACK PVC COMPOUND 956-48/1-C-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ CFR7630 resin | SABIC Innovative Plastics | PC | LEXAN™ |