Order Products : sales@su-jiao.com
ACCUCOMP™ HP0309L
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CPxgH7_ACCUCOMP-HP0309L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUCOMP™ HP0309L is a Polypropylene Homopolymer (PP Homopolymer) product. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 89 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 34.0 | MPa | |
| Break | 19.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 10 | % | |
| Break | 400 | % | |
| Flexural Modulus | 1300 | MPa | ASTM D790 |
| Flexural Strength | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 82.0 | °C | |
| 1.8 MPa, Unannealed | 53.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AR32NT6017 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Vydyne® R533 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| NOVALAST® 7001 | NOVA Polymers, Inc. | TPV | NOVALAST® |
| Dynaprene® VE5080A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| LUVOCOM® 1105-8709/GY | Lehmann & Voss & Co. | PEEK | LUVOCOM® |