Sunny® PPS 1155
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Guangdong Shunde Shunyan New Material Co., Ltd. |
| Trademark: | Sunny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CPxX4i_Sunny-PPS-1155.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyphenylene sulfide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.83 | g/cm³ | ASTM D792 |
| 23°C | 1.83 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.30 to 0.50 | % | ASTM D955 |
| 23°C | 0.30 to 0.50 | % | ISO 294-4 |
| Water Absorption | |||
| Equilibrium, 23°C | 0.010 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- 2 | 125 | MPa | ASTM D638 |
| -- | 125 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.0 | % | ASTM D638 |
| Break | 1.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span | 15500 | MPa | ASTM D790 |
| 50.0 mm Span | 16000 | MPa | ISO 178 |
| Flexural Strength | |||
| 50.0 mm Span | 209 | MPa | ASTM D790 |
| -- 4 | 215 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 74 | J/m | ASTM D256 |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 265 | °C | ASTM D648, ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 290 | °C | |
| Middle Temperature | 315 | °C | |
| Front Temperature | 330 | °C | |
| Processing (Melt) Temp | 310 | °C | |
| Mold Temperature | 140 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 50 mm span |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AR16WT6307 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| TUFNYL® SGF 15 PARKER BLUE | SRF Ltd. | Nylon 6 | TUFNYL® |
| Karina BLACK PVC COMPOUND 105800-48/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ RP003 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| Plaskon NXG-1FP | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |