OnFlex™ U 5370A-E0077
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | OnFlex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CPnFSA_OnFlex-U-5370A-E0077.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OnFlex™ U thermoplastic elastomer compounds are based on thermoplastic polyurethane elastomers (TPE-U). The OnFlex™ U 5300 series are based upon alloys of SEBS and TPU, combining the advantages of both raw materials, for example the good processability and soft haptic of a TPE-S with the excellent mechanical properties and abrasion resistance of a TPE-U. OnFlex™ U 5300 compounds are formulated to deliver very good scratch resistance, a wide hardness range and good chemical resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 35.0 | mm³ | DIN 53516 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging (100°C) | 1.1 | mg | DIN 75201B |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Odor rating | 2.10 | VDA 270 | |
| General Material Type | Thermoplastic polyurethane elastomer (TPU) |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Lateral flow : fracture, 23°C, 2.00mm | 17.7 | MPa | ISO 37 |
| Traffic : fracture, 23°C, 2.00mm | 17.7 | MPa | ISO 37 |
| Tensile Elongation 2 | ISO 37 | ||
| Lateral flow : fracture, 23°C, 2.00mm | 570 | % | ISO 37 |
| Traffic : fracture, 23°C, 2.00mm | 580 | % | ISO 37 |
| Tear Strength 3 | ISO 34-1 | ||
| Lateral flow : 23°C, 2.00mm | 47 | kN/m | ISO 34-1 |
| Traffic : 23°C, 2.00mm | 53 | kN/m | ISO 34-1 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 6 | ISO 2813 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| 各项属性值是采用注射模制基板测量得出。 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 170 - 210 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Slow |
| Note Message | |
|---|---|
| 1 . | Type 2, 200mm/min |
| 2 . | Type 2, 200mm/min |
| 3 . | Method A, pants-shaped sample, 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® 42LH-NBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| NEXT REGRIND PC/ABS MC8002-300RG | NEXT Specialty Resins, Inc. | PC+ABS | NEXT REGRIND |
| En Chuan 6123TA | En Chuan Chemical Industries Co,. Ltd. | Polyester, TS | En Chuan |
| KOPLA PA66 KDE1010 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Adstif HA3105 | LyondellBasell Industries | PP Homopolymer | Adstif |