PRESEAL® TPE 6070
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Premix Oy |
| Trademark: | PRESEAL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CPbVQP_PRESEAL-TPE-6070.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRESEAL ® TPE 6070 is a novel thermoplastic elastomer based highly conductive compound intended primarily for EMI gasketing and grounding applications. Conductivity is achieved with a silver coated glass sphere and fibre combination. PRESEAL TPE 6070 can be injection moulded like an ordinary thermoplastic elastomer thus giving great new possibilities in gasket design and mass production. It has adhesion to selected thermoplastics and insert moulding to metal is also possible. This opens interesting construction possibilities with co-injection moulding e.g. moulding the gasket directly in the phone casing. Recyclability is an added value. The material is silicone free. Typical applications include soft EMI gaskets in mobile phones, mobile phone base stations and other wireless communication environment as well as military applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.85 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 55 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2.50 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Yield | 0.400 | MPa | |
| -- | 0.300 | MPa | |
| Tensile Elongation | |||
| Yield 1 | 13 | % | ASTM D412 |
| Break | 120 | % | ISO 37 |
| Tear Strength | 3.3 | kN/m | ISO 34-1 |
| Compression Set (85°C, 24 hr) | 40 | % | ISO 815 |
| Compression Modulus | ISO 7743 | ||
| At 10% compression | 0.0340 | MPa | |
| At 15% compression | 0.0340 | MPa | |
| At 18% compression | 0.0390 | MPa |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shielding Effectiveness - 20 to 700 MHz 2 | 100 | dB | |
| Volume Resistivity 3 | 3.0E-3 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 3.0 | hr |
| Note Message | |
|---|---|
| 1 . | ISO 37 |
| 2 . | ARP 1705 |
| 3 . | Mil-G-83528 8 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-305U (Comp) | Ravago Manufacturing Americas, LLC | LLDPE | Ravago Compounds |
| Telcar® TL-2460A | Teknor Apex Company | TPE | Telcar® |
| ASTALOY™ PC/ABS TWG | Marplex Australia Pty. Ltd. | PC+ABS | ASTALOY™ |
| Crastin® SK609 BK851 | DuPont Performance Polymers | PBT | Crastin® |
| LEXAN™ 104 resin | SABIC Innovative Plastics | PC | LEXAN™ |