Generic Nylon 66+Nylon 6I/X
| Category: | Nylon 66+Nylon 6I/X , Polyamide 66 + PA 6I/X |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CPCxrv_Generic-Nylon-66-Nylon-6I-X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66+Nylon 6I/X This information is provided for comparative purposes only. |
| General Information |
|---|
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 198 to 360 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7100 to 28000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 125 to 260 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.9 to 4.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.9 to 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 to 100 | kJ/m² | ISO 179 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 to 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 5.0E+3 to 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (23°C) | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 591 to 600 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HM5303W | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Sinelec CCB2765/G | Teknor Apex Asia Pacific PTE. LTD. | PS (Specialty) | Sinelec |
| Axiall PVC 10757 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Europrene® N 2830 GRN | Versalis S.p.A. | NBR | Europrene® |
| Karina BLACK PVC COMPOUND 651-48/1-B-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |