Makrolon® SF805
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | COk01g_Makrolon-SF805.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 7.0 cm³/10 min; structural foam; 5 % glass fiber reinforced; flame retardant; high viscosity; easy release; injection molding; available in natural (opaque) and opaque colors; in combination with an appropriate blowing agent for the production of structural foam moldings |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.23 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage 2 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.55 | % | |
| Flow : 2.00 mm | 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | ISO 2039-1 | ||
| -- | 119 | MPa | |
| 6.00 mm 3 | 50.0 | MPa |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2900 | MPa | ISO 527-2/1 |
| 23°C, 6.00 mm 4 | 1800 | MPa | ISO 527-2/25 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 62.0 | MPa | |
| Break, 23°C, 6.00 mm 5 | 35.0 | MPa | |
| Break, 23°C | 60.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 4.7 | % | |
| Break, 23°C, 6.00 mm 6 | 6.0 | % | |
| Break, 23°C | 20 | % | |
| Flexural Modulus 7 | ISO 178 | ||
| 23°C, 6.00 mm 8 | 1800 | MPa | |
| 23°C | 2900 | MPa | |
| Flexural Stress 9 | ISO 178 | ||
| 3.5% Strain, 23°C | 85.0 | MPa | |
| 3.5% Strain, 23°C, 6.00 mm 10 | 55.0 | MPa | |
| 23°C | 100 | MPa | |
| 23°C, 6.00 mm 11 | 55.0 | MPa | |
| Flexural Strain at Flexural Strength | ISO 178 | ||
| 23°C 12 | 6.0 | % | |
| 23°C, 6.00 mm 13 | 5.0 | % |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | ISO 7391-PC,MFR,(,,)-09-9,GF5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 14(23°C, Complete Break) | 15 | kJ/m² | ISO 7391 |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -60°C, Complete Break | 90 | kJ/m² | |
| -30°C, Complete Break | 140 | kJ/m² | |
| -20°C, Complete Break 15 | 25 | kJ/m² | |
| -20°C, Complete Break | 160 | kJ/m² | |
| 23°C, Complete Break | 190 | kJ/m² | |
| 23°C, Complete Break 16 | 25 | kJ/m² | |
| Notched Izod Impact Strength 17(23°C, Complete Break) | 12 | kJ/m² | ISO 7391 |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 25.0 | J | |
| 23°C | 30.0 | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30°C | 4900 | N | |
| 23°C | 4300 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 0.45 MPa, Unannealed, 6.00 mm Span 18 | 133 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| 1.8 MPa, Unannealed, 6.00 mm 19 | 125 | °C | ISO 75-2/A |
| Vicat Softening Temperature | ISO 306/B50 | ||
| -- 20 | 132 | °C | |
| -- | 143 | °C | |
| Ball Pressure Test (136°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 5.5E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.0E-5 | cm/cm/°C | |
| Thermal Conductivity 21(23°C) | 0.22 | W/m/K | ISO 8302 |
| RTI Elec (3.00 mm) | 80.0 | °C | UL 746 |
| RTI Imp (3.00 mm) | 80.0 | °C | UL 746 |
| RTI Str (3.00 mm) | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 34 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.10 | ||
| 23°C, 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 8.0E-4 | ||
| 23°C, 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 175 | V | |
| Solution B | 125 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm, GY | V-0 | ||
| 6.00 mm, GY 22 | V-0 5VA | ||
| 5.00 mm, GY | 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 850 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| 4.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 825 | °C | |
| 1.50 mm | 825 | °C | |
| 3.00 mm | 825 | °C | |
| Oxygen Index 23 | 32 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Pellets |
| 2 . | 60x60x2 mm, 500 bar |
| 3 . | Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 4 . | Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 5 . | Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 6 . | Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 7 . | 2.0 mm/min |
| 8 . | Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 9 . | 2.0 mm/min |
| 10 . | Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 11 . | Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 12 . | 2 mm/min |
| 13 . | 2 mm/min, Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 14 . | Based on ISO 179-1eA, 3 mm |
| 15 . | Foamed 6.0 mm; density in the foamed state: 900 to 1000 kg/m³ |
| 16 . | Foamed 6.0 mm; density in the foamed state: 900 to 1000 kg/m³ |
| 17 . | Based on ISO 180-A, 3 mm |
| 18 . | Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 19 . | Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 20 . | 6.0 mm, Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 21 . | Cross-flow |
| 22 . | Foamed; density in the foamed state: 900 to 1000 kg/m³ |
| 23 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4004 A FR | RTP Company | PPA | RTP |
| Santoprene™ 121-85M100 | ExxonMobil Chemical | TPV | Santoprene™ |
| REVOLVE® M-56 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| Sinvicomp SIG5001 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| ALCOM® PC 740/4 GY1320-04LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |