Lucalen G3710E
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Lucalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CM4B3L_Lucalen-G3710E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucalen G3710E is a maleic anhydride grafted polyethylene resin with a high thermal stability and good flexibility. Lucalen G3710E is primarily designed to be used as the adhesive layer between the top coat polyethylene and the epoxy layer in a 3-layer coating system with easy processing charcteristics. Lucalen G3710E is available in pellet form. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.931 | g/cm³ | ISO 1183 |
| Apparent Density | > 0.50 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ISO 1133 |
| Water Content | < 0.10 | % | ISO 15512 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength | DIN 30670 | ||
| 23°C | > 20.0 | kN/m | |
| 80°C | > 4.0 | kN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 51 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 12.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | > 700 | % | ISO 527-2/50 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -56.7 | °C | ASTM D746 |
| Vicat Softening Temperature | > 100 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 125 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 215 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX 111 G7 | Taro Plast S.p.A. | PET | TAROLOX |
| NILAMID® A3 H CF30 | Nilit Plastics | Nylon 66 | NILAMID® |
| DuraGrip® DGR 6230TR | Advanced Polymer Alloys | TPE | DuraGrip® |
| LUVOCOM® 80-7858-B | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| Zetpol® 2000L | Zeon Corporation | NBR | Zetpol® |