MAJ'ECO CP564W
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CLnRdS_MAJ-ECO-CP564W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO CP564W is a 50% wood fibre reinforced polypropylene compound intended for injection moulding. MAJ'ECO CP564W has been developed especially for demanding applications in various engineering sectors. MAJ'ECO CP564W is UV stabilised. APPLICATIONS Product such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.90 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 29.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3350 | MPa | ISO 178 |
| Flexural Stress 2 | 49.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eU |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 150 - 190 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP PEI 1000 | Quadrant Engineering Plastic Products | PEI | Quadrant EPP |
| ASI POLYETHYLENE LP 477-01 | A. Schulman Inc. | HDPE | ASI POLYETHYLENE |
| Fainplast PVC RE 625 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Karina BLACK PVC COMPOUND MICRO-EX 4648/1-EXPO (**) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Silastic® Q7-7870 | Dow Corning Corporation | Silicone | Silastic® |