ACLAR® Rx20e
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | ACLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CKgOGg_ACLAR-Rx20e.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aclar® Rx20e is a 0.80 mil (20 micron) CTFE homopolymer, high performance barrier film for the pharmaceutical and medical markets. It thermoforms well on conventional blister packaging equipment and offers all of the benefits of Aclar® in a mid-range barrier material. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.11 | g/cm³ | ASTM D1505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD : 20 µm | 1400 | MPa | ASTM D882 |
| TD : 20 µm | 1340 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 89.6 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 47.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 20 µm | 120 | % | ASTM D882 |
| TD : Yield, 20 µm | 250 | % | ASTM D882 |
| Water Vapor Transmission Rate | ASTM F1249 | ||
| 20 µm, 40°C, 75% RH | 0.26 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 20 µm, 38°C, 100% RH | 0.29 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 20 µm, 25°C, 60% RH | 0.039 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 20 µm, 30°C, 60% RH | 0.062 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 211 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (20.3 µm) | < 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield, No Standard: 23.35 m²/kgTensile Strength @ Yld, ASTM D882, MD, 0.8 mil: 10000 to 16000 psiTensile Strength @ Yld, ASTM D882, TD, 0.8 mil: 5600 to 8300 psiTensile Elongation @ Yield, ASTM D882, MD, 0.8 mil: 80 to 150%Tensile Elongation @ Yield, ASTM D882, TD, 0.8 mil: 200 to 300%Secant Modulus, ASTM D882, 0.8 mil, MD: 180000 to 225000Secant Modulus, ASTM D882, 0.8 mil, TD: 175000 to 215000Tear Strength, ASTM D1004, Graves MD: 475 to 575 g/milTear Strength, ASTM D1004, Graves TD: 450 to 550 g/milCrystalline Melting Point, ASTM D4591: 211 °CDimensional Stability, ASTM D1204, MD: +8 to +12 %Dimensional Stability, ASTM D1204, TD: -8 to -12 %All film properties were tested as an average value. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GA-3133S-CCUV | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Wire & Cable |
| Unipren® Elastomers B3 NTLA010 55A UP310 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Durethan® DP 2131/20 H2.0 900051 | LANXESS GmbH | Nylon 6 | Durethan® |
| Lifoflex® UV 90 GC 1090 | ELASTO | SEBS | Lifoflex® |
| HIFOR Xtreme® SC74884 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |